Gold nanoparticles (AuNPs) have been used in a wide range of applications, conferring to bio-molecules diverse properties such as delivery, stabilization, and reduction of the adverse effects of drugs or plant extracts. Polyphenolic compounds from Bacopa procumbens (B. procumbens) (BP) can modulate proliferation, adhesion, migration, and cell differentiation, reducing the artificial scratch area in fibroblast cultures and promoting wound healing in an in vivo model. Here, chemically synthesized AuNPs conjugated with BP (AuNP-BP) were characterized using UV-Vis, ATR-FTIR, DLS, zeta-potential, and TEM analysis. The results showed an overlap of the FTIR spectra of the polyphenolic compounds from B. procumbens adhered to the surface of the AuNPs. UV-vis analysis indicated that the average size of the AuNP-BP was 28 nm, while DLS analysis showed a size of 44.58 nm and, by TEM, a size of 16.5 nm with an icosahedral morphology was observed. These measurements suggest an increase in the size of the nanoparticles after conjugation with BP, compared to the sizes of 9 nm, 44.51 nm, and 14.17 nm for the unconjugated AuNPs, respectively. Furthermore, the zeta potential of the AuNPs, which was originally -36.3 ± 12.3 mV shifted to -18.2 ± 7.02 mV after conjugation with BP, indicating improved stability of the nanoparticles. Enhancement of the wound healing effect was evaluated by morphometric, histochemical, and FTIR changes in a rat wound excision model. Results showed that the nanoconjugation process reduced the BP concentrations by 100-fold to have the same wound healing effect as BP alone. Besides, histological and FTIR spectroscopy analyses demonstrated that AuNP-BP treatment exhibited better macroscopical performance, showing a reduction in inflammatory cells and an increased synthesis and improved organization of collagen fibers.
Keywords: FTIR analyses of wound repair tissue; polyphenolic-gold nanoparticles conjugates; wound healing model.