In this study, conversion coatings were produced on the AM50 magnesium alloy by a plasma electrolytic oxidation (PEO) process in alkaline-silicate electrolyte with the addition of potassium hexafluorophosphate, using a unipolar pulse power source. The coating microstructure and its composition were determined using scanning electron microscopy (SEM) and an X-ray photoelectron spectroscopy (XPS). The corrosion resistance of the conversion coatings was evaluated by means of potentiodynamic polarization tests (PDP) and electrochemical impedance spectroscopy (EIS) in a dilute Harrison solution (DHS). It has been found that the properties (microstructure, composition, and coating thickness) of the obtained layer and, therefore, their anticorrosive resistance strongly depend on the electrolyte composition. The best anticorrosive properties were observed in the layers obtained in the presence of 2.5 g/L KPF6. It was found that the conversion coating produced with the addition of hexafluorophosphate is characterized by a different morphology (sponge-like) and better anticorrosion properties, in comparison to the coating obtained with the addition of fluoride and orthophosphate salts commonly used in PEO synthesis. The sponge-like structure, which is similar to bone structure in combination with the presence of phosphates in the layer, can increase the biocompatibility and the possibility of self-healing of this coating. However, neither Mg(PF6)2, nor any other compounds containing PF6-, have been found in the layers produced.
Keywords: corrosion resistance; magnesium alloy; microstructure; plasma electrolytic oxidation.