This study describes a methodology to prepare and characterize PUF [poly(urea formaldehyde)] microcapsules containing 5-ethylidene-2-norbornene (ENB) as self-healing agent, as well as the compatibility evaluation of ENB in the presence of Grubb's catalyst with an epoxy matrix. First, the results of an adhesion assay by lap shear proved chemical compatibility between the epoxy matrix and self-healing agent in the presence of Grubb's catalyst. After evaluating the chemical compatibility, microcapsules with ENB were synthesized in an oil-in-water emulsion system. Thereafter, the microcapsules were morphologically, chemically and thermally characterized in which a granulometric dispersion between 30-140 μm and an average size of 69.8 ± 4.9 μm were observed. The SEM (scanning electron microscope) results showed that the average thickness of microcapsules shell was 3.6 ± 0.4 μm. The thermogravimetric analysis (TGA) showed that microcapsules are susceptible to rupture and consequent ENB release in temperatures greater than 230 °C, demonstrating that microcapsules are suitable for applications in materials with self-healing capacity.