Green Synthesis of CoZn-Based Metal-Organic Framework (CoZn-MOF) from Waste Polyethylene Terephthalate Plastic As a High-Performance Anode for Lithium-Ion Battery Applications

Yaxin Wang; Kong Meng; Huimin Wang; Yongheng Si; Kun Bai; Shaorui Sun

doi:10.1021/acsami.3c15792

Green Synthesis of CoZn-Based Metal-Organic Framework (CoZn-MOF) from Waste Polyethylene Terephthalate Plastic As a High-Performance Anode for Lithium-Ion Battery Applications

ACS Appl Mater Interfaces. 2024 Jan 10;16(1):819-832. doi: 10.1021/acsami.3c15792. Epub 2023 Dec 20.

Authors

Yaxin Wang¹, Kong Meng¹, Huimin Wang¹, Yongheng Si¹, Kun Bai¹, Shaorui Sun¹

Affiliation

¹ Beijing Key Laboratory for Green Catalysis and Separation, The Faculty of Environment and Life, Beijing University of Technology, Beijing 100124, PR China.

PMID: 38117931
DOI: 10.1021/acsami.3c15792

Abstract

The recycling of discarded polyethylene terephthalate (PET) plastics produced metal-organic frameworks can effectively minimize environmental pollution and promote sustainable economic development. In this study, we developed a method using NaOH in alcohol and ether solvent environments to degrade PET plastics for synthesizing terephthalic acid. The method achieved a 97.5% degradation rate of PET plastics under a reaction temperature of 80 °C for 60 min. We used terephthalic acid as a ligand from the degradation products to successfully synthesize two types of monometallic and bimetallic CoZn-MOF materials. We investigated the impact of different metal centers and solvents on the electrochemical performance of the MOF materials. The result showed that the MOF-DMF/H₂O material maintained a specific capacity of 1485.5 mAh g^-1 after 100 cycles at a current density of 500 mA g^-1, demonstrating excellent rate capability and cycling stability. In addition, our finding showed that the performance difference might be attributed to the synergistic effect of bimetallic Co²⁺ and Zn²⁺ in MOF-DMF/H₂O, rapid lithium-ion diffusion and electron transfer rates, and the absence of coordinating solvents. Additionally, the non-in situ X-ray powder diffraction, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy analysis results showed that lithium storage in the MOF-DMF/H₂O electrode mainly depended on the aromatic C6 ring and carboxylate portions of the organic ligands in different charge and discharge states. Lithium ions can be reversibly inserted/removed into/from the electrode material. The physical adsorption on the MOF surface through electrostatic interactions enhanced both capacity and cycling stability. This research provides valuable insight for mitigating solid waste pollution, promoting sustainable economic development, and advancing the extensive applications of MOF materials in lithium-ion batteries.

Keywords: anode materials; lithium storage; lithium-ion battery; metal−organic frameworks; polyethylene terephthalate.