Purpose: The purpose of this in vitro study was to compare the tensile bond strength (TBS) of resin nanoceramics (RNC), zirconia, and lithium disilicate (LS2) restorations cemented to titanium abutments before and after thermomechanical aging.
Materials and methods: Twelve specimens per group were fabricated to determine the TBS between a titanium abutment and four types of crown materials (2 RNCs, LS2, and translucent zirconia crowns for the maxillary molar). After milling, the abutments and crowns were cemented with resin cement after air-particle abrasion. In addition, thermomechanical aging (200,000 cycles, 50 N, 2 Hz) was applied to half of the specimens by using a mastication simulator. TBS was measured by using a universal testing machine. The interface between the crown and the cement was observed by using scanning electron microscopy (SEM). Two-way ANOVA was performed to analyze the effects of crown materials and thermomechanical aging. Failure-mode and interface analyses were also conducted.
Results: After thermomechanical aging, the TBS decreased in the LS2 specimens and increased in RNCs (p < 0.001). The ratio of mixed failure and debonding with the hole-sealing resin increased in the RNC group. SEM images showed the reduced gap between the crown and the resin cement after thermomechanical aging in the RNC group.
Conclusions: Differences in TBS were affected by the crown materials after thermomechanical aging. After thermomechanical aging, the RNC crowns showed increased TBS, whereas LS2 and zirconia crowns exhibited decreased or similar TBS.
Keywords: resin cement; resin nanoceramics; tensile bond strength; thermomechanical aging; zirconia.