The fly ash-based geopolymer (FABG) containing slag has distinct advantages in field applications. In this work, given that the activator modulus is a significant parameter affecting the properties of FABG, the influence mechanism of activator modulus (SiO2/Na2O from 1.1 to 1.5) on the macro-mechanical properties and micro-structure composition of FABG containing slag is explored. According to the experimental results, the early product of FABG containing slag is mainly C-A-S-H gel, and N-(C)-A-S-H gel with high cross-linking degree is formed at a later stage. Both C-A-S-H and N-A-S-H gels are distinguished in reaction products by using 29Si NMR. The Si/Al ratio of N-A-S-H gel and C-A-S-H gel decreases with the increase of modulus, resulting in an increase of MCL in C-A-S-H. Appropriate activator modulus can effectively activate slag and fly ash to yield more gels and form a more uniform and dense micro-structure, resulting in a lower threshold pore size and macroporosity, and an associated increase of the material strength. Meanwhile, the gel amount has a positive effect on the strength development in the FABG.
Keywords: Activator modulus; Fly ash–based geopolymer; Macro-mechanics; Micro-structure.
© 2023. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.