A nanoporous silver film (npAgF), a promising structure for surface-enhanced Raman spectroscopy (SERS), can be fabricated by using successive O2 and Ar plasma treatments on a planar silver film. The common dealloying method for producing an npAgF involves annealing at high temperatures to produce an alloy film, as well as harsh etching using corrosive chemicals. By contrast, the plasma-based method can be applied directly to various functional substrates to produce more sophisticated npAgF structures. Herein, we report a facile fabrication method for a wrinkled npAgF (w-npAgF) for SERS applications using a thermally contractible polystyrene substrate. The w-npAgF had 3D wrinkles of the nanoporous structure and showed approximately 8 times higher SERS enhancement than did the flat npAgF. Moreover, the w-npAgF could be reused for multiple SERS measurements of different molecules by mild O2 and Ar plasma treatments after each use, in which the O2 plasma effectively removed the adsorbed organic molecules and the Ar plasma reduced silver oxide to pristine silver for subsequent SERS measurements. The wrinkled nanoporous structure was maintained after multiple mild plasma treatments for reuse. The simplicity of plasma-based fabrication and high sensitivity of w-npAgFs are promising features for the green production of low-cost and reusable 3D SERS substrates.
© 2023 The Authors. Published by American Chemical Society.