The present study was aimed at synthesis of polymeric hydrogels for controlled boron (B) release, as B deficiency is a major factor that decreases crops yield. Thus, graphene oxide incorporated guar gum and poly (ethylene glycol) hydrogels were prepared using the Solution Casting method for boron release. 3-Glycidyloxypropyl trimethoxysilane (GLYMOL) was used as a cross-linker. Characterizations of hydrogels were carried out by Fourier Transform Infrared Spectroscopy (FTIR), Thermo-Gravimetric Analysis and Scanning Electron scope. The FTIR outcomes confirmed the existence of functional groups, bindings and development of hydrogel frameworks from incorporated components. The quantity of GLYMOL directly increased the thermal stability and water retention but decreased the swelling %. The maximum swelling for the hydrogel formulations was observed at pH 7. The addition of GLYMOL changed the diffusion from quasi-Fickcian to non-Fickcian diffusion. The maximum swelling quantities of 3822% and 3342% were exhibited by GPP (control) and GPP-8 in distilled water, respectively. Boron release was determined in distilled water and sandy soil by azomethine-H test using UV-Visible spectrophotometer while 85.11% and 73.65% boron was released from BGPP-16, respectively. In short, water retentive, water holding capacities, swelling performances, biodegradability and swelling/deswelling features would offer an ideal platform for boron release in sustained agricultural applications.
Keywords: boron release; graphene oxide; guar gum; hydrogels; poly (ethylene glycol); sustained agriculture.
© 2023 The Authors.