Flexible electrodes are becoming a topic of interest for a range of applications including implantation. They can be used for neural signal recording and for electrical stimulation of atrophying muscles. Unlike the traditionally used metal electrodes that are harsh to the body's tissues, flexible electrodes conduct electricity while preserving the delicate tissues. Polydimethylsiloxane (PDMS), a non-conductive synthetic polymer characterized by its flexibility, low cost, biocompatibility, and durability during implantation, has been explored as a matrix for flexible electrodes. This study reports the synthesis of composite boronic acid-modified carbon dots (BA-CDs)/PDMS electrode materials. The performance of the composite electrode is evaluated electrochemically (for its conductivity and charge storage capacity) and mechanically (Young's modulus). Furthermore, the effect of increasing the PDMS crosslinking density on the electrode's performance is studied based on the hypothesis that a higher crosslinking will bring the BA-CDs closer together, thereby facilitating the movement of electrons. Results of this study showed that incorporating 10% BA-CDs dispersed with 16% glycerol in 74% PDMS with a higher crosslinking density resulted in a bulk impedance of 47.7 Ω and a conductivity of 2.68×10-3 S/cm, both of which surpassed that of the same composition with lower crosslinking. The synthesized flexible electrode material was capable of charge storage although the charge storage capacity (0.00365 mC/cm2) was lower than the safe limit for some tissue activation. Furthermore, the electrode maintained a modulus of elasticity (0.2322 MPa) that is compatible with biological soft tissues.Clinical Relevance- This study reports a conductive electrode that has a flexibility compatible with that of biological tissues for future purposes such as neural signal recording and tissue electrical stimulation (e.g. atrophying muscles). The reported BA-CD/PDMS electrode overcomes the limitations of the harsh metals previously used as implantable electrodes that harm the biological tissues due to their high rigidity.