This paper analyses the key findings of a study devoted to PET-modified bitumen. The research program was run according to the D-optimal experimental plan based on a factorial design. Five factors, i.e., the type of polymer (source), the type of bitumen (qualitative factors), PET amount, mixing rate, and mixing temperature (quantitative factors), controlled the bitumen-polymer mixing process. The experiment included a series of determinations of bitumen's rheological characteristics obtained by MSCR (Jnr, R) and G*/sin(δ) at 50 °C, 60 °C, and 70 °C. The low-temperature properties of the composite (critical temperature) were evaluated using a BBR test. The findings showed that bitumen modification with PET primarily reduced the creep susceptibility of the bituminous-polymer mixture. The low-temperature characteristics of the modified bitumen played a secondary but essential role. The amount of polymer and the mixing rate interacted with the temperature, significantly reducing the stiffness of the composite, while the type and amount of bitumen had a substantial effect on the results obtained in the BBR test. It is worth noting that when combining bitumen and plastomer, special attention should be paid to ensuring a high level of homogeneity of the mixture by controlling the parameters of the mixing process accordingly. The tests and analyses provided crucial models (GLM), which allowed for the prediction of the plastomer-modified bitumen's low- and high-temperature properties. The resulting relationships between factors and the identification of their impact on the bitumen properties enable a better understanding of the process of bitumen modification with PET. The conclusions presented here serve as a basis for future optimisation of the modified bitumen composition. The performed studies indicate that the use of >3% plastomer in bitumen 70/100 allows for a reduction in its susceptibility (MSCR) to below 0.5 kPa-1, making it suitable for bituminous mixtures for high-traffic roads. No significant increase in critical temperature (BBR) was observed.
Keywords: bitumen modification; rheological properties; statistical modelling; waste polymers.