Rare-earth-free permanent magnets with the L10 phase are actively researched for their potential as a future class of magnetic materials, capable of operating at higher temperatures and in challenging corrosion environments such as renewable energy applications. Among these classes, MnGa shows potential, being cost effective and having interesting magnetic properties. A MnGa magnetic alloy, with composition Mn73.6Ga26.4 in atomic percent, was produced via the out-of-equilibrium method, and its structural and magnetic properties were assessed using X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED) and extended magnetic characterization. We show that the MnGa alloy submitted to thermal annealing in optimal conditions exhibits a two-phase microstructure, where small nanocrystals of tetragonal L10/D022 magnetic phase are embedded within a D019 MnGa matrix of a non-collinear antiferromagnetic nature. These co-existing, magnetically different phases produce an optimal set of promising magnetic properties, larger than the values reported in the literature for single-phase MnGa alloys and thin films. Such large values are explained by the exchange coupling between competing non-collinear magnetic sublattices of the D019 MnGa with the net moment of the small magnetic nanocrystals of tetragonal symmetry.
Keywords: MnGa tetragonal phase; magnetic properties; rare earth free magnets.