2D layered magnets, such as iron chalcogenides, have emerged these years as a new family of unconventional superconductors and provided the key insights to understand the phonon-electron interaction and pairing mechanism. Their mechanical properties are of strategic importance for the potential applications in spintronics and optoelectronics. However, there is still a lack of efficient approach to tune the elastic modulus despite the extensive studies. Herein, the modulated elastic modulus of 2D magnetic FeTe and its thickness-dependence is reported via phase engineering. The grown 2D FeTe by chemical vapor deposition can present various polymorphs, that is tetragonal FeTe (t-FeTe, antiferromagnetic) and hexagonal FeTe (h-FeTe, ferromagnetic). The measured Young's modulus of t-FeTe by nanoindentation method shows an obvious thickness-dependence, from 290.9 ± 9.2 to 113.0 ± 8.7 GPa when the thicknesses increased from 13.2 to 42.5 nm, respectively. In comparison, the elastic modulus of h-FeTe remains unchanged. These results can shed light on the efficient modulation of mechanical properties of 2D magnetic materials and pave the avenues for their practical applications in nanodevices.
Keywords: FeTe; Young's modulus; elastic properties; nanoindentation; phase modulation.
© 2023 Wiley‐VCH GmbH.