In this comprehensive study, Ce-doped ZnO nanostructures were hydrothermally synthesized with varying Ce concentrations (0.5%, 1.0%, 1.5%, and 2.0%) to explore their gas-sensing capabilities, particularly towards NO2. Structural characterization revealed that as Ce doping increased, crystal size exhibited a slight increment while band gap energies decreased. Notably, the 0.5% Ce-doped ZnO nanostructure demonstrated the highest NO2 gas response of 8.6, underscoring the significance of a delicate balance between crystal size and band gap energy for optimal sensing performance. The selectivity of the 0.5% Ce-doped ZnO nanostructures to NO2 over other gases like H2, acetone, NH3, and CO at a concentration of 100 ppm and an optimized temperature of 250 °C was exceptional, highlighting its discriminatory prowess even in the presence of potential interfering gases. Furthermore, the sensor displayed reliability and reversibility during five consecutive tests, showcasing consistent performance. Long-term stability testing over 30 days revealed that the gas response remained almost constant, indicating the sensor's remarkable durability. In addition to its robustness against humidity variations, maintaining effectiveness even at 41% humidity, the sensor exhibited impressive response and recovery times. While the response time was swift at 11.8 s, the recovery time was slightly prolonged at 56.3 s due to the strong adsorption of NO2 molecules onto the sensing material hindering the desorption process. The study revealed the intricate connection between Ce-doping levels, structure, and gas-sensing. It highlighted the 0.5% Ce-doped ZnO nanostructure as a highly selective, reliable, and durable NO2 gas sensor, with implications for future environmental monitoring and safety.
Keywords: Ce-doped ZnO; Gas sensing; High-sensitivity; NO(2) detection; Selectivity.
Copyright © 2023 Elsevier Ltd. All rights reserved.