Fe-N-C (iron-nitrogen-carbon) electrocatalysts have emerged as potential alternatives to precious metal-based materials for the oxygen reduction reaction (ORR). However, the structure of these materials under electrochemical conditions is not well understood, and their poor stability in acidic environments poses a formidable challenge for successful adoption in commercial fuel cells. To provide molecular-level insights into these complex phenomena, we combine periodic density functional theory (DFT) calculations, exhaustive treatment of coadsorption effects for ORR reaction intermediates, including O and OH, and comprehensive analysis of solvation stabilization effects to construct voltage-dependent ab initio thermodynamic phase diagrams that describe the in situ structure of the active sites. These structures are further linked to activity and stability descriptors that can be compared with experimental parameters such as the half-wave potential for ORR and the onset potential for carbon corrosion and CO2 evolution. The results indicate that pyridinic Fe sites at zigzag carbon edges, as well as other edge sites, exhibit high activity for ORR compared to sites in the bulk. However, edges neighboring the active sites are prone to instability via overoxidation and consequent site loss. The results suggest that it could be beneficial to synthesize Fe-N-C catalysts with small sizes and large perimeter edge lengths to enhance ORR activity, while voltage fluctuations should be limited during fuel cell operation to prevent carbon corrosion of overoxidized edges.
Keywords: Fe-N-C catalysts; density functional theory; fuel cells; oxygen reduction reaction.