Poly(dicyclopentadiene) (poly-DCPD) is a thermoset with potential for high-performance applications. In this research, epoxy resin was blended with different concentrations of fly ash class F particles at 0.0, 1.0, 10.0, and 50.0 wt.%, aiming to improve its use as a high-volume structural material by decreasing costs and reducing its negative environmental impact through using fly ash particles. A planetary Thinky mixer was used to initially mix the resin with the curing agent, followed by incorporating a Grubbs catalyst. The microstructures were analyzed using scanning electron microscopy (SEM), where particles were found to be homogeneously distributed over the polymer matrix. The thermomechanical behavior was evaluated via curing, compression, dynamic mechanical analysis (DMA), and thermo-gravimetric analysis (TGA). Nanoindentation tests were also conducted. Fly ash was found to decelerate the curing of the resin through the release of calcium ions that enhanced the exothermic reaction.
Keywords: mechanical properties; nanoindentation; polymer composites; reinforcements.