The purpose of this study was to investigate the effects of different peri-implantitis treatment methods (Er,Cr:YSGG laser, diode laser, and electrocautery) on various titanium implant surfaces: machined; sandblasted, large-grit, and acid-etched; and femtosecond laser-treated surfaces. Grade 4 titanium (Ti) disks, with a diameter of 10 mm and a thickness of 1 mm, were fabricated and treated using the aforementioned techniques. Subsequently, each treated group of disks underwent different peri-implantitis treatment methods: Er,Cr:YSGG laser (Biolase, Inc., Foothill Ranch, CA, USA), diode laser (Biolase, Inc., Foothill Ranch, CA, USA), and electrocautery (Ellman, Hicksville, NY, USA). Scanning electron microscopy, energy-dispersive X-ray spectroscopy, and wettability were used to characterize the chemical compositions and surfaces of the treated titanium surfaces. Significant changes in surface roughness were observed in both the electrocautery (Sa value of machined surface = 0.469, SLA surface = 1.569, femtosecond laser surface = 1.741, and p = 0.025) and Er,Cr:YSGG laser (Ra value of machined surface = 1.034, SLA surface = 1.380, femtosecond laser surface = 1.437, and p = 0.025) groups. On femtosecond laser-treated titanium implant surfaces, all three treatment methods significantly reduced the surface contact angle (control = 82.2°, diode laser = 74.3°, Er,Cr:YSGG laser = 73.8°, electrocautery = 76.2°, and p = 0.039). Overall, Er,Cr:YSGG laser and electrocautery treatments significantly altered the surface roughness of titanium implant surfaces. As a result of surface composition after different peri-implantitis treatment methods, relative to the diode laser and electrocautery, the Er,Cr:YSGG laser increased oxygen concentration. The most dramatic change was observed after Er:Cr;YSGG laser treatment, urging caution for clinical applications. Changes in surface composition and wettability were observed but were not statistically significant. Further research is needed to understand the biological implications of these peri-implantitis treatment methods.
Keywords: dental implant; electrocautery treatment; laser treatment; surface roughness.