2D Ti3C2-MXene Serving as Intermediate Layer between Absorber and Back Contact for Efficient CZTSSe Solar Cells

Qiong Ma; Xin-Pan Cui; Wen-Hui Zhou; Dong-Xing Kou; Zheng-Ji Zhou; Yue-Na Meng; Ya-Fang Qi; Sheng-Jie Yuan; Li-Tao Han; Si-Xin Wu

doi:10.1021/acsami.3c11262

2D Ti₃C₂-MXene Serving as Intermediate Layer between Absorber and Back Contact for Efficient CZTSSe Solar Cells

ACS Appl Mater Interfaces. 2023 Dec 6;15(48):55652-55658. doi: 10.1021/acsami.3c11262. Epub 2023 Nov 22.

Authors

Affiliation

¹ The Key Laboratory for Special Functional Materials of MOE, School of Materials, National & Local Joint Engineering Research Center for High-efficiency Display and Lighting Technology, Collaborative Innovation Center of Nano Functional Materials and Applications, Henan University, Kaifeng 475004, China.

PMID: 37991928
DOI: 10.1021/acsami.3c11262

Abstract

Kesterite Cu₂ZnSn(S,Se)₄ (CZTSSe) has been considered as the most promising absorber material for inorganic thin-film solar cells. Among the three main interfaces in CZTSSe-based solar cells, the CZTSSe/Mo back interface plays an essential role in hole extraction as well as device performance. During the selenization process, the reaction between CZTSSe and Mo is one of the main reasons that lead to a large open circuit voltage (V_OC) deficit, low short circuit current (J_sc), and fill factor. In this study, 2D Ti₃C₂-MXene was introduced as an intermediate layer to optimize the interface between the CZTSSe absorber layer and Mo back contact. Benefiting from the 2D Ti₃C₂-MXene intermediate layer, the reaction between CZTSSe and Mo was effectually suppressed, thus, significantly reducing the thickness of the detrimental Mo(S,Se)₂ layer as well as interface recombination at the CZTSSe/Mo back interface. As a result, the power conversion efficiency of the champion device fabricated with the 2D Ti₃C₂-MXene intermediate layer was improved from 10.89 to 13.14% (active-area efficiency). This study demonstrates the potential use of the 2D Ti₃C₂-MXene intermediate layer for efficient CZTSSe solar cells and promotes a deeper understanding of the back interface in CZTSSe solar cells.

Keywords: CZTSSe; MXene; back contact; interface recombination; intermediate layer.