In this study, the use of anionic polymerization for the synthesis of living poly(dimethylsiloxane) or PDMS-Li+, as well as poly(2-vinylpyridine) or P2VP-Li+ homopolymers, and the subsequent use of chlorosilane chemistry in order for the two blocks to be covalently joined leading to PDMS-b-P2VP copolymers is proposed. High vacuum manipulations enabled the synthesis of well-defined materials with different molecular weights (Μ¯n, from 9.8 to 36.0 kg/mol) and volume fraction ratios (φ, from 0.15 to 0.67). The Μ¯n values, dispersity indices, and composition were determined through membrane/vapor pressure osmometry (MO/VPO), size exclusion chromatography (SEC), and proton nuclear magnetic resonance spectroscopy (1H NMR), respectively, while the thermal transitions were determined via differential scanning calorimetry (DSC). The morphological characterization results suggested that for common composition ratios, lamellar, cylindrical, and spherical phases with domain periodicities ranging from approximately 15 to 39 nm are formed. A post-polymerization chemical modification reaction to quaternize the nitrogen atom in some of the P2VP monomeric units in the copolymer with the highest P2VP content, and the additional characterizations through 1H NMR, infrared spectroscopy, DSC, and contact angle are reported. The synthesis, characterization, and quaternization of the copolymer structure are important findings toward the preparation of functional materials with enhanced properties suitable for various nanotechnology applications.
Keywords: P2VP; PDMS; anionic polymerization; chlorosilane chemistry; divergent Tgs; high χ copolymers; quaternization; self-assembly behavior.