The effective utilization rate of river-dredged silt was extremely low, and common disposal methods such as dumping it into the ocean have already threatened the ecological environment. To demonstrate that dredged silt can be used as a mineral admixture to modify magnesium potassium phosphate cement (MKPC), the mechanical properties and hydration degree of sintered silt ash (SSA)-blended MKPC in the early stage of hydration were studied systematically in this paper, with MKPC as the reference group. The mechanical experiment results showed that in the process of increasing the SSA content to 25%, the compressive strength first increased and then decreased. Among the samples, the compressive strength of cement aged by 1d and 3d with 15% content was the highest, which increased by 11.5% and 17.2%, respectively, compared with the reference group. The setting time experiment found that with the increase in SSA content, the hydration reaction rate of MKPC slowed down significantly. Its effect of delaying hydration was most obvious when the SSA content was 10-15%. The X-ray diffraction pattern showed that there was no large amount of new crystalline substances formed in the hydration product. The results obtained by scanning electron microscopy show that the microstructure tended to be denser and the hydration products tended to be plump when the SSA content was in the range of 0-15%. The non-contact electrical resistivity experiment showed that the addition of SSA delayed the early hydration of MKPC. Combined with the above experiment results, it was found that when the content of SSA was less than 15%, it not only delayed the early hydration of MKPC, but also deepened its hydration degree.
Keywords: early-age cement; hydration degree; magnesium potassium phosphate cement; mechanical properties; sintered silt ash.