The paper presents research on multicomponent glasses obtained from natural and secondary raw materials, i.e., basalt, amphibolite, and cullet. The raw materials were used as potential sets to produce mineral fibres or glass-ceramic materials. FTIR spectroscopy and XRD studies were carried out to identify the composition of the phase type in the glass sets. The results were supported by SEM-EDS microstructural studies of the obtained materials. The ability of the melts to crystallize and their basic properties required in producing mineral fibres, i.e., the hardness and the acidity modulus, were also determined. In the glass samples after the crystallization process, the spectroscopic studies revealed an increase in the half-width of the band at 1200-800 cm-1 and splitting at the values of about 870 cm-1 and 970 cm-1. These changes probably indicate the formation of pyroxene-type crystalline phases. Moreover, based on the XRD results, it was confirmed that the obtained materials were fully amorphous. After annealing at 800 °C for 2 h, the materials show a small proportion of crystalline phases. For the materials annealed at higher temperatures, clear peaks from the crystalline phases were represented mainly by pyroxenes. The proportion of crystalline phases in the samples was also found to rise with increasing temperature, and the hardness values for the basalt glasses and glasses after crystallization rose from 753 to 946 HV0.05. Such an effect positively affects the properties of the obtained glass-ceramic materials based on the proposed sets. However, in the case of mineral fibres, crystallization at early 2 h at 800 °C can be a disadvantageous feature from the point of view of their application because crystalline phases can lead to fibre damage after a short period of operation; this will be confirmed in this study.
Keywords: FTIR spectroscopy; glass-ceramic materials; mineral fibres; multicomponent glasses; pyroxenes.