In this study, the microstructural behavior of the advanced Ti-5.7Al-3.8Mo-1.2Zr-1.3Sn-0.15Si (VT8M-1) alloy during rotary swaging (RS) was investigated. VT8M-1 has increased heat resistance and is considered a replacement for the Ti-6Al-4V alloy. It was shown that, during RS, the evolution of the primary a phase is characterized by the formation of predominantly low-angle boundaries according to the mechanism of continuous dynamic recrystallization. The density of low-angle boundaries increases three times: from 0.38 µm-1 to 1.21 µm-1 after RS. The process of spheroidization of the lamellar (a + b) component is incomplete. The average size of globular a and b particles was 0.3 μm (TEM). It is shown that the microstructures after RS (ε = 1.56) and equal-channel angular pressing (ECAP) (ε = 1.4) are significantly different. The temperature-velocity regime and the predominance of shear deformations during ECAP contributed to a noticeable refinement of the primary a-phase and a more complete development of globularization of the lamellar (a+b) component. EBSD studies have shown that RS leads to the formation of a structure with a higher density of low- and high-angle boundaries compared to the structure after ECAP. The results are useful for predicting alloy microstructure in the production of long rods that are further used in forging operations.
Keywords: electron backscatter diffraction (EBSD); microstructure; rotary swaging; second-phase particles; titanium alloy; ultrafine-grained structure.