High-entropy alloys (HEAs) are significantly promising candidates for heterogeneous catalysis, yet the controllable synthesis of ultrafine HEA nanoparticles (NPs) remains a formidable challenge due to severe thermal sintering during the high-temperature fabrication process. Herein, we report a sulfur-stabilizing strategy to construct ultrafine HEA NPs with an average diameter of 4.02 nm supported on sulfur-modified Ti3C2Tx (S-Ti3C2Tx) MXene, on which the strong interfacial metal-sulfur interactions between HEA NPs and the S-Ti3C2Tx supports significantly increase the interfacial adhesion strength, thus greatly suppressing nanoparticle sintering by retarding both particle migration and metal atom diffusion. The representative quinary PtPdCuNiCo HEA-S-Ti3C2Tx exhibits excellent catalytic performance toward alkaline ethanol oxidation reaction (EOR) with an ultrahigh mass activity of 7.03 A mgPt+Pd-1, which is 4.34 and 5.17 times higher than those of the commercial Pt/C and Pd/C catalysts, respectively. In situ attenuated total reflection-infrared spectroscopy studies reveal that the high intrinsic catalytic activity for the EOR can be ascribed to the synergy of different catalytically active sites of HEA NPs and the well-designed interfacial metal-sulfur interactions.
Keywords: MXene; ethanol oxidation reaction; high-entropy alloy; metal−support interactions; sulfur stabilizing.