Synthesis and application of novel microporous framework of nanocomposite from trona for photocatalysed degradation of methyl orange dye

Abstract

Photocatalysed degradation of environmental contaminants is one of the most fashionable technologies in the purification of water because the method converts toxic products to nontoxic ones. In this study, a method has been developed to synthesize novel nanocomposites of Na-Ca-Al-Si oxides for the first time. The average surface area, pore volume and pore size for the novel product were 1742.55 m²/g, 0.3499 cc/g and 3.197 nm respectively. The crystal parameters were a = 7.1580 Å, b = 7.4520 Å, c = 7.7160 Å, α = 115.0600, β = 107.3220, γ = 100.4380, density (calculated) = 2.0 × 10³g/cm³ and cell volume = 332.7 ų respectively. The average crystalline size deduced from the Scherrer equation (i.e. 6.9393 nm) was higher than the value of 1.024 nm obtained from the graphical method. The FTIR and UV spectra of the nanocomposites were unique and provided baseline information that characterises the new product. XRD profiling of the new product reveals the existent of a silica framework consisting of NaAlSi₃O₃ and CaAl₂Si₂O₈ The synthesized nanocomposites is an effective photocatalyst for the degradation of methyl orange dye in water, with aoptimum efficiency of 96% at an initial dye concentration of 10 ppm, the adsorbent dosage of 0.5 g,contact time of 90 min and pH of 2.5. The Langmuir-Hinshelwood, modified Freundlich and pseudo-second kinetic models were significant in the description of the photocatalytic kinetics of the degraded dye molecules.

Keywords: Catalysis; Degradation; Dye; Mixed metal oxide nanocomposites; Remediation; Water contamination.