Antimony triselenide (Sb2 Se3 ) has possessed excellent optoelectronic properties and has gained interest as a light-harvesting material for photovoltaic technology over the past several years. However, the severe interfacial and bulk recombination obviously contribute to significant carrier transport loss thus leading to the deterioration of power conversion efficiency (PCE). In this work, buried interface and heterojunction engineering are synergistically employed to regulate the film growth kinetic and optimize the band alignment. Through this approach, the orientation of the precursor films is successfully controlled, promoting the preferred orientational growth of the (hk1) of the Sb2 Se3 films. Besides, interfacial trap-assisted nonradiative recombination loss and heterojunction band alignment are successfully minimized and optimized. As a result, the champion device presents a PCE of 9.24% with short-circuit density (JSC ) and fill factor (FF) of 29.47 mA cm-2 and 63.65%, respectively, representing the highest efficiency in sputtered-derived Sb2 Se3 solar cells. This work provides an insightful prescription for fabricating high-quality Sb2 Se3 thin film and enhancing the performance of Sb2 Se3 solar cells.
Keywords: Sb2Se3 solar cells; carrier transport; efficiency; nonradiative recombination losses.
© 2023 Wiley-VCH GmbH.