Alkali-activated slag (AAS) presents a promising alternative to ordinary Portland cement due to its cost effectiveness, environmental friendliness, and satisfactory durability characteristics. In this paper, cow dung waste was recycled as a renewable natural cellulose fiber, modified with alkali, and then added to AAS mortar. The physico-chemical characteristics of raw and modified cow dung fibers were determined through Fourier transform infrared (FTIR), X-ray diffraction (XRD), and Scanning electron microscope (SEM). Investigations were conducted on the dispersion of cow dung fibers in the AAS matrix, as well as the flowability, strength, and autogenous shrinkage of AAS mortar with varying cow dung fiber contents. The results indicated that modified fiber has higher crystallinity and surface roughness. The ultrasonic method showed superior effectiveness compared to pre-mixing and after-mixing methods. Compared with raw cow dung fibers, modified fibers led to an increase of 11.3% and 36.3% of the 28 d flexural strength and compressive strength of the AAS mortar, respectively. The modified cow dung fibers had a more significant inhibition on autogenous shrinkage, and the addition of 2 wt% cow dung fibers reduced the 7 d autogenous shrinkage of the AAS paste by 52.8% due to the "internal curing effect." This study provides an alternative value-added recycling option for cow dung fibers as a potential environmentally friendly and sustainable reinforcing raw material for cementitious materials, which can be used to develop low autogenous shrinkage green composites.
Keywords: alkali treatment; alkali-activated slag; autogenous shrinkage; cow dung fibers; ultrasonication.