This manuscript shows the study of the structure, mechanical, and chemical properties of high-entropy borides MeB2 (Me = Ti, Ta, Nb, Hf, Zr). High-entropy borides were synthesized by mechanical alloying and spark plasma sintering. A chemically homogeneous powder with a low iron content (0.12%) was obtained in a planetary mill by rotating the planetary disk/pots at 200-400 rpm and a processing time of 7.5 h. The structure, mechanical, and chemical properties of the resulting high-entropy borides have been studied. A single-phase hexagonal structure is formed during spark plasma sintering of mechanically alloyed powders at 2000 °C. The microhardness of the samples ranged from 1763 to 1959 HV. Gas-dynamic tests of the synthesized materials showed that an increase in the content of Zr and Hf in the composition increases the thermal-oxidative resistance of the material.
Keywords: ceramics; high-entropy borides; mechanical alloying; spark plasma sintering; thermal-oxidative resistance.