Wire arc additive manufacturing (WAAM) was employed to fabricate 4043 aluminum alloy walls. To investigate the effects of sinusoidal, triangular, and rectangular waveforms of alternating current (AC) and their transients on the wall geometry, microstructure evolution, hardness, and wear properties were evaluated. The root mean square (RMS) current value was maximum for the rectangular and minimum for the triangular waveform. The section produced by the triangular waveform had the highest height-to-width ratio, indicating that this waveform can be a favorable choice for creating components using WAAM. The optical micrographs of the transverse cross-section of the printed sections revealed the grain structure produced with this waveform to be heterogeneous, having a columnar dendritic structure at the bottom and equiaxed at the top portion. The waveforms also had an impact on the hardness and wear characteristics of all the walls, which were attributed to their cooling rate.
Keywords: aluminum alloy; microstructure; waveforms; wire arc additive manufacturing.