Recent technological advancements led to the development of various plasma-based technologies for post-packaging modifications. The purpose of the present preclinical in vivo study was to assess the safety and efficacy of a novel chairside nonthermal gas plasma treatment for enhancing osseointegration of titanium implants. Six male mixed foxhounds underwent extraction of mandibular premolars and first molars, and the sockets healed for 42 days. Canine mandibles were randomized to receive either plasma-treated (test) or non-plasma-treated (control) dental implants. A total of 36 implants were placed in six animals, and they were sacrificed at 2 weeks (two animals), 4 weeks (two animals), and 6 weeks (two animals) after the implant surgery. When the radiographic analysis was performed, the changes in bone level were not statistically significant between the two groups at 2 weeks and 4 weeks. The difference became significant at 6 weeks (p = 0.016), indicating more bone loss from baseline to 6 weeks for the control group. The bone-to-implant contact (BIC) appeared to be higher for the test groups at all time points, and the BIC was significantly higher for the test group at 4 weeks (p = 0.046). In conclusion, this study underscored the potential of nonthermal plasma treatment in enhancing implant osseointegration.
Keywords: bone-to-implant contact; dental implant; histology; histomorphometic analysis; osseointegration; plasma treatment; sandblasted large grit acid-etched surface.