Fretting-corrosion is one of the failure processes in many applications, including biomedical implants. For example, the modern design of hip implants with multiple components offers better flexibility and inventory storage. However, it will trigger the fretting at the implant interfaces with a small displacement amplitude (< 5 µm) and usually in a partial slip region. Although many studies have been reported on the fretting, they have high displacement amplitude and are in the gross slip region. It is imperative to have an apparatus to overcome such limitations, specifically for hip implant applications. Therefore, this study describes the development of a fretting-corrosion apparatus with low micro-motion (≤ 5 µm) that can simultaneously monitor the corrosion process. Initial experiments with Ti6Al4V-Ti6Al4V in 0.9% saline, Ti6Al4V-Ti6Al4V in bovine calf serum (BCS), and ZrO2-Ti6Al4V in BCS were conducted to validate the system. As a result, the fretting regime of all groups remained partially slip region throughout the 3600 cycles, and the possible failure mechanisms are proposed in this manuscript.
Keywords: Fretting apparatus; Fretting-corrosion; hip implant; micromotions.