Spinel-structured LiNix Mn2-x O4 (LNMO), with low-cost earth-abundant constituents, is a promising high-voltage cathode material for lithium-ion batteries. Even though extensive electrochemical investigations have been conducted on these materials, few studies have explored correlations between their loss in performance and associated changes in microstructure. Here, down to the atomic scale, the structural evolution of these materials is investigated upon the progressive cycling of lithium-ion cells. Transgranular cracking is revealed to be a key feature during cycling; this cracking is initiated at the particle surface and leads to the penetration of electrolytes along the crack path, thereby increasing particle exposure to the electrolyte. The lattice structure on the crack surface shows spatial variances, featuring a top layer of rock-salt, a sublayer of a Mn3 O4 -like arrangement, and then a mixed-cation region adjacent to the bulk lattice. The transgranular cracking, along with the emergence of local lattice distortion, becomes more evident with extended cycling. Further, phase transformation at primary particle surfaces and void formation through vacancy condensation is found in the cycled samples. All these features collectively contribute to the performance degradation of the battery cells during electrochemical cycling.
Keywords: cathode-electrolyte interface; high-voltage spinel cathodes; surface phase transformation; transgranular cracking; void formation.
© 2023 The Authors. Small published by Wiley-VCH GmbH.