The increasing emissions of gaseous pollutants of anthropogenic origin, such as carbon dioxide (CO2), which causes global warming, have raised great interest in developing and improving processes that allow their mitigation. Among them, adsorption on porous materials has been proposed as a sustainable alternative. This work presents a study of CO2 equilibrium adsorption at low temperatures (0, 10, and 20 °C) over a wide range of low pressures, on activated carbon derived from Eucalyptus (ES) and Patula pine (PP) forest waste, and carbonaceous material derived from waste tires (WT). The precursors of these materials were previously prepared, and their physicochemical properties were characterized. ES and PP were thermochemically treated with phosphoric acid, and WT was oxidized with nitric acid. Additionally, these materials were used to obtain monoliths using uniaxial compaction techniques and different binding agents, with better results obtained with montmorillonite. A total of six adsorbent solids had their textural and chemical properties characterized and were tested for CO2 adsorption. The highest specific surface area (1405 m2 g-1), and micropore properties were found for activated carbon derived from Eucalyptus whose highest adsorption capacity ranged from 2.27 mmol g-1 (at 0 °C and 100 kPa) to 1.60 mmol g-1 (at 20 °C and 100 kPa). The activated carbon monoliths presented the lowest CO2 adsorption capacities; however, the studied materials showed high potential for CO2 capture and storage applications at high pressures. The isosteric heats of adsorption were also estimated for all the materials and ranged from 16 to 45 kJ mol-1 at very low coverage explained by the energetic heterogeneity and weak repulsive interactions among adsorbed CO2 molecules.
Keywords: Activated carbons; CO2 adsorption; Chemical activation; Lignocellulosic precursor; Monoliths; Pyrolysis; Waste tires.
© 2023. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.