The copolymer ethylene-octene (POE) has good aging resistance and is an inexpensive asphalt additive compared to the styrene-butadiene-styrene copolymer (SBS). However, POE is easy to segregate in asphalt during storage at high temperatures. Grafting glycidyl methacrylate (GMA) onto the molecular backbone of POE (i.e., POE-g-GMA) may solve this problem, for the epoxy groups in GMA can react with the active groups in asphalt. Asphalt modified with linear and crosslinked POE-g-GMA were prepared, and the hot storage stability, physical properties and thermal oxidation aging properties were discussed in detail. The results show that linear and low-degree crosslinked POE-g-GMA-modified asphalts are storage-stable at high temperatures via measurements of the difference in softening points and small-angle X-ray scattering (SAXS) characterizations from macro and micro perspectives. The difference in softening points (ΔSP) between the upper and lower ends is no more than 3.5 °C for modified asphalts after 48 h of being in an oven at 163 °C. More importantly, the crosslinking modification of POE-g-GMA can further increase the softening point and reduce the penetration as well as rheological properties via conventional physical property, dynamic shear rheometer (DSR) and multiple-stress creep recovery (MSCR) tests. Furthermore, asphalt modified with crosslinked POE-g-GMA reveals better aging resistance via measurements of the performance retention rate and electron paramagnetic resonance (EPR) characterizations after a rolling thin film oven test (RTFOT). This work may provide further guidelines for the application of polymers in asphalt.
Keywords: asphalt; crosslinking modification of POE-g-GMA; physical properties; storage stability; thermal oxidation aging resistance.