Supercritical impregnation of starch aerogels with quercetin: Fungistatic effect and release modelling with a compartmental model

Abstract

This work proposes the use of supercritical CO₂ to impregnate starch (potato and corn) aerogels with quercetin for a potential fungistatic application. Starch aerogels were successfully produced with supercritical drying, but different results were found depending on the amylose/amylopectin ratio. A higher amount of amylose increases aerogels' specific surface area (with a structure with nanofibrils and nodes) due to the linear and amorphous character of this polymer, whereas a higher amount of amylopectin decreases this property until values of only 25 m²·g^-1, obtaining an aerogel with a rough surface. These results were explained with XRD, thermogravimetric, and rheological results (triple step with two temperature sweeps and a time sweep and steady state analysis) concerning hydrogel formation. In fact, retrogradation step plays a more important role in hydrogel formation for a starch source with a higher amount of amylopectin due to an increase in the different polymers' interactions. Supercritical impregnation of quercetin on the aerogels was successfully performed (a loading around 0.30 % with respect to the amount of polymer), and in vitro results indicated that the aerogels produced a fungistatic effect on different types of fungi, but only in the first 12 h because the microorganisms adapted to the surrounding environment. Finally, a compartmental model was used to fit the drug release, which is controlled by quercetin aqueous solubility, indicating the main mass transfer resistances (mass transfer through aerogels was always around 500 min^-1 and dissolution process mass transfer from 5·10^-3 to 1.65·10^-3 s^-1) and how an increase in the specific surface area of the aerogels (in the case of corn aerogel) provided a stronger initial burst (70-80 % in 20 min). In fact, this initial burst release was mathematically related to a parameter, that varies from 0.178 to 0.036 depending on the aerogel composition. This study shows that starch aerogels can be impregnated with a hydrophobic compound with fungistatic effect by using supercritical CO₂, modifying in addition the drug release by changing the native starch.

Keywords: Aerogels; Rheological measurements; Supercritical fluids; Supercritical impregnation.