Chameleons are famous for their quick color changing abilities, and it is commonly assumed that they do this for camouflage. However, recent reports revealed that chameleons also change color for body temperature regulation. Inspired by the structure of the panther chameleon's skin, a stripe-patterned poly(N-isopropylacrylamide) (PNIPAM) and polyacrylamide (PAM) hydrogel film with a laminated structure is fabricated in this work; thus, both camouflage and thermoregulation can be achieved through controlling Vis and NIR light effectively. For the PNIPAM stripe, the upper layer is the native PNIPAM hydrogel and the lower layer is the carbon nanotube-composited PNIPAM hydrogel. Thus, the PNIPAM stripe is capable of reaching 28 °C at a low environmental temperature (12 °C) and a low radiation intensity (20 mW cm-2), while preventing the body temperature from rising by changing to white under a strong radiation intensity (100 mW cm-2). For the PAM stripe, the upper layer combines colloidal photonic crystals and displays a tunable structural color by stretching, and the lower layer is mixed with PNIPAM microgels for thermal regulation. Through the fabrication of multifunctional patterns, the film can achieve both dynamic structural color and thermoregulation by precisely controlling solar radiation absorption, scattering, and reflection. More importantly, in the stripe-patterned system, the shrinkage of the PNIPAM stripes can effectively trigger the elongation of the PAM stripe, which endows the structural color changing process to be self-powered completely. The performances show that the stripe-patterned film may have potential applications in intelligent coatings, especially in areas with large temperature differences during the day such as high plains.
Keywords: camouflage; stripe-patterned film; thermoregulation; thermoresponsive hydrogel/microgel; tunable structural color.