Increasing the energy density of lithium-ion batteries, and thereby reducing costs, is a major target for industry and academic research. One of the best opportunities is to replace the traditional graphite anode with a high-capacity anode material, such as silicon. However, Si-based lithium-ion batteries have been widely reported to suffer from a limited calendar life for automobile applications. Heretofore, there lacks a fundamental understanding of calendar aging for rationally developing mitigation strategies. Both open-circuit voltage and voltage-hold aging protocols were utilized to characterize the aging behavior of Si-based cells. Particularly, a high-precision leakage current measurement was applied to quantitatively measure the rate of parasitic reactions at the electrode/electrolyte interface. The rate of parasitic reactions at the Si anode was found 5 times and 15 times faster than those of LiNi0.8Mn0.1Co0.1O2 and LiFePO4 cathodes, respectively. The imbalanced charge loss from parasitic reactions plays a critical role in exacerbating performance deterioration. In addition, a linear relationship between capacity loss and charge consumption from parasitic reactions provides fundamental support to assess calendar life through voltage-hold tests. These new findings imply that longer calendar life can be achieved by suppressing parasitic reactions at the Si anode to balance charge consumption during calendar aging.
Keywords: Si anode; calendar aging; charge balance; parasitic reactions; steady leakage current.