A novel poly (lactic acid) (PLA) composite with excellent mechanical properties, toughness, thermal stability, and water resistance was developed using a reactive melt-blending technique. PLA was melt mixed with epoxy resin (EPOXY) and bamboo pulp (PULP) to improve its reaction and mechanical properties. FTIR analysis confirmed the successful reaction of the PLA/EPOXY/PULP composites; the epoxy groups of EPOXY reacted with the -COOH groups of PLA and the -OH groups of PULP. The PLA/EPOXY/PULP5 composite showed a high tensile strength (67 MPa) and high toughness of 762 folding cycles, whereas the highest tensile strength was 77 MPa in the PLA/EPOXY5/PULP20 sample. SEM images presented a gap between the PLA and PULP; gap size decreased with the addition of EPOXY. The Tg of the PLA decreased with the EPOXY plasticizer effect, whereas the Tm did not significantly change. PULP induced crystallinity and increased Vicat softening of the PLA/PULP and PLA/EPOXY/PULP composites. The EPOXY reaction of the PLA/PULP composites improved their tensile properties, toughness, thermal stability, and water resistance.
Keywords: bamboo pulp; epoxy resin; poly (lactic acid); reaction; reactive into cross-linking reaction; reactive melt blending.