This paper presents sustainable technology for environmentally friendly composite production. Biobased unsaturated polyester resin (b-UPR), synthesized from waste polyethylene terephthalate (PET) glycosylate and renewable origin maleic anhydride (MAnh) and propylene glycol (PG), was reinforced with unmodified and vinyl-modified biosilica nanoparticles obtained from rice husk. The structural and morphological properties of the obtained particles, b-UPR, as well as composites, were characterized by Fourier-transform infrared spectroscopy (FTIR), nuclear magnetic resonance spectroscopy (NMR), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) techniques. The study of the influence of biosilica modification on the mechanical properties of composites was supported by hardness modeling. Improvement of the tensile strength of the b-UPR-based composite at 2.5 wt.% addition of biosilica modified with vinyl silane, named "b-UPR/SiO2-V" composite, has been achieved with 88% increase. The thermal aging process applied to the b-UPR/SiO2-V composite, which simulates use over the product's lifetime, leads to the deterioration of composites that were used as fillers in commercial unsaturated polyester resin (c-UPR). The grinded artificially aged b-UPR composites were used as filler in c-UPR for the production of a table top layer with outstanding mechanical properties, i.e., impact resistance and microhardness, as well as fire resistance rated in the V-0 category according to the UL-94 test. Developing sustainable composites that are chemically synthesized from renewable sources is important from the aspect of preserving the environment and existing resources as well as the extending their life cycle.
Keywords: biosilica; mechanical properties; polymer–matrix composites (PMCs); recycling.