Mulching is a common practice for improving crop yield and obtaining an out-of-season production, but when made using plastic materials it can bring environmental problems due to the management and the disposal of films at the end of the cropping seasons. To increase the sustainability of this practice, recently, mulching films made with biodegradable organic materials have become more widely used. Our aim was to evaluate the effect of a biodegradable mulching film on yield and qualitative traits of the San Marzano tomato fruits over two years (2014 and 2015). Two different types of mulching were tested: (i) black biodegradable film (MB12) and (ii) black low-density polyethylene (LDPE) were compared to bare soil (BS). Both mulching films elicited a 25% increase in yield, mainly due to the significantly higher number of fruits per square meter, compared to BS. Both mulching films also elicited a 9.9% increase in total soluble solids and a 57% increase in carotenoid content, while firmness showed the highest value in BS fruits. MB12 determined the highest value of the Hunter color ratio a/b of tomato fruits, followed by LDPE, while the lowest value was recorded in BS fruits. Both mulching films elicited an increase of 9.6%, 26.0%, and 11.7% for flavonoids, polyphenols, and AsA, respectively. In 2014, the MB12 degradation started at 71 days after transplant (DAT); in 2015, at 104 DAT. Therefore, replacing polyethylene with biodegradable film would seem to be an agronomically efficient and environmentally sustainable practice.
Keywords: antioxidant activity; ascorbic acid; carotenoids; flavonoids; polyphenols; sustainable agricultural practices.