The goal of this study was to evaluate the pH and the release of calcium from four calcium-silicate-based cements.
Methods: Four materials were tested (ProClinic MTA; Angelus MTA; ProRoot MTA; Biodentine). The palatal canal root of acrylic upper molars was filled with each cement. Afterwards, they were set in phosphate-buffered saline. Measurements were taken by atomic adsorption spectroscopy (AAS) at 3, 24, 72, 168, 336, 672, and 1008 h. The pH was measured at the same timepoints. Kruskal-Wallis tests were carried out in each period, as the Kolmogorov-Smirnov and Shapiro-Wilk tests showed no parametric results.
Results: Significant differences (p < 0.05) in calcium release were found at the 3-, 24-, and 72-hour evaluations. All of the analyzed groups presented a release of calcium ions up to 168 h, and the general tendency was to increase up to 672 h, with a maximum release of 25.45 mg/g in the ProRoot group. We could only observe significant differences (p < 0.05) in pH value over 168 h between the Biodentine (7.93) and Angelus MTA (7.31) groups.
Conclusions: There were significant differences (p < 0.05) in calcium release. Nevertheless, no significant differences (p > 0.05) in the pH values were found at the studied timepoints, except for the values at 168 h.
Keywords: MTA; biomaterial; calcium-silicate-based cements; ion release; mineral trioxide aggregate; pH.