This study investigates the cyclic load application impact on fly-ash-based geopolymer composites that are reinforced with a low amount of fibre reinforcement. For reinforcement purposes, polyvinyl alcohol and steel fibres are used. For testing purposes, four geopolymer composite mixes were made, three of which had fibre reinforcement. Simultaneously, specimens were tested for shrinkage, static-load-induced creep, and cyclic-load-induced creep. For static and cyclic creep testing, specimens were loaded with 20% of their strength. For cyclic creep testing, load application and release cycles were seven days long. When each cycle was introduced, the load was applied in steps. Necessary load application or unloading lasted for 5 min and consisted of four steps, each 25% of the necessary load. From the long-term static and cyclic creep tests, it was seen that only the plain specimens showed that static creep strains are within cyclic creep strains. For all the other specimens, the static load was higher than the cyclic-load-induced creep amplitude. Also, 1% polyvinyl alcohol fibre-reinforced specimens showed the most elastic characteristics under cyclic load, and 1% steel fibre-reinforced specimens appeared to be the most resistant to the cyclic load introduction.
Keywords: fibre-reinforced geopolymer; fly-ash-based geopolymer composite; long-term properties under cyclic load.