The reliable fabrication of polycrystalline zeolitic imidazolate framework (ZIF) membranes continues to pose challenges for their industrial applications. Here, we present a vapor-phase seeding approach that integrates atomic layer deposition (ALD) with ligand vapor treatment to synthesize ZIF membranes with high propylene/propane separation performance. This method began with depositing a ZnO coating onto the support surface via ALD. The support underwent treatment with 2-methylimidazole vapor to transform ZnO to ZIF-8, forming the seed layer. Subsequent secondary growth was employed at near-room temperature, allowing the seeds to grow into a continuous membrane. ZIF-8 membranes made on macroporous ceramic support by this method consistently demonstrated propylene permeances above 1 × 10-8 mol Pa-1 m-2 s-1 and a propylene/propane separation factor exceeding 50. Moreover, we demonstrated the effectiveness of the vapor-phase seeding method in producing the ZIF-67 membrane.
Keywords: ZIF membrane; atomic layer deposition; membrane formation; propylene/propane separation; vapor-phase synthesis.