Temperature-controlled 3D cryoprinting (TCC) is an emerging tissue engineering technology aimed at overcoming limitations of conventional 3D printing for large organs: (a) size constraints due to low print rigidity and (b) the preservation of living cells during printing and subsequent tissue storage. TCC addresses these challenges by freezing each printed voxel with controlled cooling rates during deposition. This generates a rigid structure upon printing and ensures cell cryopreservation as an integral part of the process. Previous studies used alginate-based ink, which has limitations: (a) low diffusivity of the CaCl2 crosslinker during TCC's crosslinking process and (b) typical loss of print fidelity with alginate ink. This study explores the use of an ink made of agar and alginate to overcome TCC protocol limitations. When an agar/alginate voxel is deposited, agar first gels at above-freezing temperatures, capturing the desired structure without compromising fidelity, while alginate remains uncrosslinked. During subsequent freezing, both frozen agar and alginate maintain the structure. However, agar gel loses its gel form and water-retaining ability. In TCC, alginate crosslinking occurs by immersing the frozen structure in a warm crosslinking bath. This enables CaCl2 diffusion into the crosslinked alginate congruent with the melting process. Melted agar domains, with reduced water-binding ability, enhance crosslinker diffusivity, reducing TCC procedure duration. Additionally, agar overcomes the typical fidelity loss associated with alginate ink printing.
Keywords: alginate–agar gel; dual solidification; microstructure; temperature-controlled cryoprinting.