Background: The purpose of this in vitro study was to evaluate the effect of different adhesion primers on the repair bond strength of bulk-fill resin composite and short-term hydrolytic stability of the repair interface before and after accelerated aging. In addition, direction of debonding stress was examined.
Materials and methods: Bulk-fill substrates were aged in water for 14 days at 37 °C. Smooth resin composite surfaces were prepared for the substrates with a superfine grinding paper (FEPA #500, #1200, #2000). Test specimens were produced by attaching bulk-fill composite to the substrate surfaces, using three different primer/bonding systems. Specimens were aged 24 h at 37 °C in water, or thermal cycled (5-55 °C/5,000 cycles). Subsequently, shear bond strength and micro-tensile bond strength were evaluated. In total there were 60 specimens for the shear bond strength and 60 specimens for the micro-tensile bond strength measurements (30 stored in water 24 h, 30 thermal cycled, n = 10 in each primer/bonding mode).
Results: The mean shear bond strength was 9.1-13.1 MPa after 24 h water storage and 6.9-10.7 MPa after thermal cycling. The mean micro-tensile bond strength was 28.7-45.8 MPa after 24 h water storage and 22.7-37.9 MPa after thermal cycling.
Conclusion: The Ceramic primer (silane containing) seems to perform better than the three-step etch and rinse adhesive or the Composite primer. Shear-type stress had an adverse effect on the repair bond strength of bulk-fill resin composites.
Keywords: Bonding; bulk-fill; micro-tensile bond strength; shear bond strength.