Articular cartilage defects comprise a spectrum of diseases associated with degeneration or damage of the connective tissue present in particular joints, presenting progressive osteoarthritis if left untreated. In vitro tissue regeneration is an innovative treatment for articular cartilage injuries that is attracting not only clinical attention, but also great interest in the development of novel biomaterials, since this procedure involves the formation of a neotissue with the help of material support. In this work, functional alginate and waterborne polyurethane (WBPU) scaffolds have been developed for articular cartilage regeneration using 3D bioprinting technology. The particular properties of alginate-WBPU blends, like mechanical strength, elasticity and moistening, mimic the original cartilage tissue characteristics, being ideal for this application. To fabricate the scaffolds, mature chondrocytes were loaded into different alginate-WBPU inks with rheological properties suitable for 3D bioprinting. Bioinks with high alginate content showed better 3D printing performance, as well as structural integrity and cell viability, being most suitable for scaffolds fabrication. After 28 days of in vitro cartilage formation experiments, scaffolds containing 3.2 and 6.4 % alginate resulted in the maintenance of cell number in the range of 104 chondrocytes/scaffold in differentiated phenotypes, capable of synthesizing specialized extracellular matrix (ECM) up to 6 μg of glycosaminoglycans (GAG) and thus, showing a potential application of these scaffolds for in vitro regeneration of articular cartilage tissue.
Keywords: 3D bioprinting; Alginate; Bioink; Chondrocytes cartilage tissue engineering; Waterborne polyurethane.
Copyright © 2023. Published by Elsevier B.V.