Horseradish peroxidase (HRP)-mediated extrusion bioprinting has a significant potential in tissue engineering and regenerative medicine. However, they often face challenges in terms of printing fidelity and structural integrity when using low-viscosity inks. To address this issue, a method that alternately extrudes bioinks and support material was developed in this study. The bioinks consisting of cells, HRP, and phenolated polymers, and the support material contained hydrogen peroxide (H2O2). The support material not only prevented the collapse of the constructs but also supplied H2O2 to facilitate the enzymatic reaction. 3D constructs with tall and complex shapes were successfully printed from a low-viscosity ink containing 10 U/mL HRP and 1.0% w/v phenolated hyaluronic acid (HA-Ph), with a support material containing 10 mM H2O2. Over 90% viability of mouse fibroblasts (10T1/2) was achieved following the printing process, along with a morphology and proliferation rate similar to that of nontreated cells. Furthermore, human hepatoblastoma (HepG2) cells showed an increased spheroid size over 14 days in the printed constructs. The 10T1/2 cells adhered and proliferated on the constructs printed from inks containing both phenolated gelatin and HA-Ph. These results demonstrate the great potential of this HRP-mediated extrusion bioprinting technique for tissue engineering applications.
Keywords: bioprinting; horseradish peroxidase; hyaluronic acid; hydrogel; phenolic hydroxyl moiety; support material.