Lithium (Li) metal anodes have become an important component of the next generation of high energy density batteries. However, the Li metal anode still has problems such as Li dendrite growth and unstable solid electrolyte interface layer. Herein, we present a functional electrolyte additive (PANHF) successfully synthesized from acrylonitrile and hexafluorobutyl methacrylate via a polymerization reaction. With extensive analytical characterization, it is found that the PANHF can improve the reversibility and Coulombic efficiency of the Li deposition/dissolution reaction and prevent the growth of Li dendrites by forming a solid electrolyte interphase rich in organic matter on the outer layer and LiF on the inner layer. The results show that the cycling performance of the Li/Li cell was greatly improved in the electrolyte containing 0.5 wt % PANHF. Specifically, the cycling stability of more than 700 cycles was achieved at a current density of 1.0 mA cm-2. Moreover, the Li/NCM811 cell with 0.5 wt % PANHF has a higher capacity of 137.7 mA h g-1 at 1.0 C and a capacity retention of 83.41% after 200 cycles. This work highlights the importance of protecting the Li metal anode with functional bipolymer additives for next-generation Li metal batteries.
Keywords: Li deposition/dissolution reaction; Li metal anode; electrolyte additives; polymerization; solid electrolyte interphase.