Most rubber products come from petrochemical resources, which are increasingly in short supply. Rubber products that formed irreversible chemical bonds in the vulcanization process are difficult to recycle, resulting in a serious waste of resources. Therefore, it is important to prepare a kind of reprocessable biobased elastomers. Using furfuryl methacrylate (FMA) as the modified monomer, poly(dibutyl itaconate-myrcene-furfuryl methacrylate) (PDBIMFA) was synthesized by high-temperature emulsion polymerization successfully. The structure and compositions of PDBIMFA were characterized by Fourier transform infrared and 1H NMR, and the effects of different FMA contents on the structures and properties of PDBIMFA were systematically studied. Based on the Diels-Alder reaction, bismaleimide (BMI) and carbon black (CB) were introduced into PDBIMFA as cross-linking agents and reinforcing fillers, respectively, by the melt blending method, and PDBIMFA-BMI elastomer materials and CB/PDBIMFA-BMI elastomer composites with thermo-reversible cross-linking characteristics were prepared. The effects of the ratio of FMA and BMI on the mechanical properties of PDBIMFA-BMI were studied. PDBIMFA-BMI and CB/PDBIMFA-BMI were reprocessed twice, and the recovery rate of tensile strength was both more than 90%. The addition of CB was found to play a reinforcing role in the elastomer and with the introduction of the amount of CB, the reprocessability of composite remained at a good level. It is hoped that this research will provide a new strategy for the sustainable development of bio-based elastomer materials.
© 2023 The Authors. Published by American Chemical Society.