The purpose of this study was to evaluate the color stability of repaired aesthetic restorative resin matrix materials after immersion in coffee and the effect of polishing systems after staining. One hundred and eighty cylindrical discs (8 mm × 2 mm) were prepared using a conventional nano-fill resin composite (Clearfil Majesty Esthetic A2 shade) with round cavities (3 × 1 mm). Cavities were repaired by three resin composite materials: Clearfil Majesty Esthetic A2 shade, one-shaded nano-fill resin composite (Omnichroma) and group-shaded nano-hybrid resin composite (Optishade, medium shade). Each group was polished with three polishing systems (n = 20); aluminum oxide (Soflex Spiral Wheels, 3M ESPE), silicon carbide (Occlubrush, Kerr, CA, USA) and diamond particulate (Twist Dia Spiral Wheels, Kuraray, Okayama, Japan). Color change (ΔE00) measurements were performed with a spectrophotometer at the baseline. Half of the polished samples were either kept in distilled water or immersed in coffee for 15 days, and color measurements were repeated before and after polishing. Statistical analysis was performed using the Kruskal-Wallis test. Repaired samples showed different color correspondence values in all groups. All three restorative materials showed significant color changes (ΔE00) after immersion in coffee (p ≤ 0.05). Repolishing of stained samples showed color improvement values in all groups. The content of the polishing system played an important role in removing the stains.
Keywords: color measurement; polishing systems; universal composite resins.