The hydrolysis of the phosphonate ester linker during the synthesis of hybrid (organic-inorganic) TiO2 nanoparticles is important when forming porous hybrid organic-inorganic metal phosphonates. In the present work, a method was utilized to control the in-situ partial hydrolysis of diphosphonate ester in the presence of a titania precursor as a function of acid content, and its impact on the hybrid nanoparticles was assessed. Organodiphosphonate esters, and more specific, their hydrolysis degree during the formation of hybrid organic-inorganic metal oxide nanoparticles, are relatively under explored as linkers. Here, a detailed analysis on the hydrolysis of tetraethyl propylene diphosphonate ester (TEPD) as diphosphonate linker to produce hybrid TiO2 nanoparticles is discussed as a function of acid content. Quantitative solution NMR spectroscopy revealed that during the synthesis of TiO2 nanoparticles, an increase in acid concentration introduces a higher degree of partial hydrolysis of the TEPD linker into diverse acid/ester derivatives of TEPD. Increasing the HCl/Ti ratio from 1 to 3, resulted in an increase in degree of partial hydrolysis of the TEPD linker in solution from 4 % to 18.8 % under the applied conditions. As a result of the difference in partial hydrolysis, the linker-TiO2 bonding was altered. Upon subsequent drying of the colloidal TiO2 solution, different textures, at nanoscale and macroscopic scale, were obtained dependent on the HCl/Ti ratio and thus the degree of hydrolysis of TEPD. Understanding such linker-TiO2 nanoparticle surface dynamics is crucial for making hybrid organic-inorganic materials (i. e. (porous) metal phosphonates) employed in applications such as electronic/photonic devices, separation technology and heterogeneous catalysis.
Keywords: NMR spectroscopy; hybrid TiO2 nanoparticles; linker-nanoparticle binding; organodiphosphonate esters; partial hydrolysis.
© 2023 Wiley-VCH GmbH.