Characterization of an Iron-Copper Bimetallic Metal-Organic Framework for Adsorption of Methyl Orange in Aqueous Solution

Abstract

Iron-based organic frame material MIL-53 (Fe) was synthesized by the hydrothermal method with Cu²⁺ incorporated to obtain bimetallic composite MIL-53 (Fe, Cu). The structure and morphology of the material were characterized by SEM, XRD, BET, FTIR, XPS, and zeta potential. The adsorption performance of MIL-53 (Fe, Cu) on methyl orange was tested under a variety of conditions, including the effects of pH and material dosage, by the static adsorption test. The results show that under the condition of pH = 7, a temperature of 30°C, and an adsorbent dosage of 20 mg, the removal rate of MIL-53 (Fe, Cu) for methyl orange can reach more than 96% within 4 h, and the maximum adsorption capacity after fitting by the thermodynamic model can reach 294.43 mg/g, showing the excellent adsorption performance of MIL-53 (Fe, Cu) on methyl orange. In addition, by exploring the adsorption mechanism of MIL-53 (Fe, Cu) on methyl orange, it is found that the adsorption of MIL-53 (Fe, Cu) on methyl orange depends on chemical adsorption, as evidenced by combining Fe³⁺ and Cu²⁺ in the material with methyl orange molecules to form complexes to achieve adsorption. While the specific surface area of the material had no obvious effect on adsorption, the effects of pH, temperature, and concentration were explored. At a pH of 6.5, greater adsorption occurred at higher temperatures, as determined by thermodynamic model fitting, as well as with higher initial methyl orange molecule concentration.